Poly Vinyl Formal Pvf Foam

Scanning electron microscopy showed that the pvf foams had two kinds of pore structures closed and open cell.

Poly vinyl formal pvf foam.

Outstanding solution absorbing performance unique high rate hydroexpansivity and promising biocompatibility. And the highest α value of 0 98 was obtained at 2000 hz for pvf 3 0. Morphology observation showed that the porous structure of pvf foams was successfully created using water as the blowing agent and it was strongly affected by the crosslinking agent and polymer concentration leading to an easily tuned pore size from hundreds of microns to few microns. Formvar refers to any of several thermoplastic resins that are polyvinyl formals which are polymers formed from polyvinyl alcohol and formaldehyde as copolymers with polyvinyl acetate they are typically used as coatings adhesives and molding materials.

Poly vinyl formal pvf of 90 acetalization was prepared by acid catalysed homogeneous formalization of pva of molecular weight 14 000 with paraformaldehyde. Find sigma aldrich 182680 msds related peer reviewed papers technical documents similar products more at sigma aldrich. 3 1 1 polyvinyl formal pvf. The formation of the formal was.

It was found that a higher pva concentration prevented foam volume shrinkage and the best concentration was 16 wt. 2 shows the infrared absorption spectra of 12 mm thick polyvinyl formal foil irradi ated with 900 mev au ions at room temperature rt. Developed a double crosslinking sodium alginate sa polyvinyl formal pvf composite with ipn structure. Ir spectroscopy results on pvf and its polymeric subunits pva and pvac are discussed in detail.

The state key laboratory of polymer materials engineering polymer research institute of sichuan university chengdu 610065 china new materials r d center institute of chemical material china academy of engineering physics mianyang 621900 china. Formvar used to be the registered trade name of the polyvinyl formal resin produced by monsanto chemical company in st. The sound absorption coefficient α of the pvf foam largely increased with the decreasing pore size especially in the frequency range of 800 2500 hz. The pvf foams could be used as sound absorbing materials because of the open cell multiporous structures.

The modulus of the composite increased 1857 and the highest volume expansivity reached 2150.